Zinc Coating Thickness Requirements: ASTM A vs. F Dimension. ASTM A ASTM F Avg. Coating. Thickness of. Specimens. Tested. 23 Feb ASTM F covers the requirements for hot-dip zinc coating applied to carbon steel and alloy steel bolts, screws, washers, nuts, and special. ASTM F – Download as PDF File .pdf), Text File .txt) or read online.

Author: Samugrel Nishicage
Country: Belgium
Language: English (Spanish)
Genre: Education
Published (Last): 14 May 2016
Pages: 362
PDF File Size: 12.34 Mb
ePub File Size: 1.30 Mb
ISBN: 784-5-68601-553-7
Downloads: 61815
Price: Free* [*Free Regsitration Required]
Uploader: Keshakar

Galvanizing fasteners in accordance with A, will usually meet or exceed the requirements of F, because F defers to A in many sections.

The amount of additional documentation beyond ASTM Astm f2329 requirements will vary depending astm f2329 a number of optional requirements the customer can specify under F According to Note C of Table 1, It is only required to conduct testing on samples for coating thickness once every five batch lots. Therefore, it must be clarified whether the plant has the ability to lubricate hardware after hot-dip galvanizing. The test methods for appearance and smoothness under F shall be conducted for every batch lot astm f2329 visual inspection in accordance with methods provided in A F defines the two astm f2329 lots and their associated sampling plans as follows:.

The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other.

ASTM F2329

Nails and rivets are not included in this specification. See astm f2329 of Table 1 below. Combining values from the two systems may result in non-conformance with the standard.

Astm f2329 Item s – proposed revisions of this standard. Zinc Coating Thickness Requirements: ASTM F describes two different sampling plans for batch lots and production lots. Best practice is to note the bath temperature when galvanizing steel to Astm f2329, although only the average bath temperature is required.

ASTM F vs. ASTM A | American Galvanizer’s Association

Furthermore, there are two types of production lots: The temperatures used in the hot-dip galvanizing astm f2329 typically do not appreciably alter the mechanical properties of steel, but there f329 some instances when there are potential concerns. This abstract is a brief summary of astm f2329 referenced standard.

It is important to note the acceptance criterion in all cases is zero defects. For example, a astm f2329 size of articles under the detection process requires testing of 11 samples astm f2329 zstm thickness, 11 samples for visual appearance, and 3 samples for adhesion. Link to Active This link will always route to the current Active version of the standard. Otherwise, a third party will be required to apply the lubricant at an additional cost.

Suppliers shall furnish certified test results from astm f2329 the shipping lots originated.

On the other hand, if embrittlement testing is necessary under F, it is to astm f2329 conducted per ASTM F a wedge positioned and tensioned under a bolt headwhich is a different method than any of the methods described within A Paragraph 9. If certified test reports are astm f2329 available, then the supplier must default to Sample Size C and conduct the tests required.

It is important to ensure the customer specifies which type of astm f2329 is required. Authored by Alana Hochstein.

Table 2 of F lists average coating thickness requirements for production lots, batch lots, and individual specimens. The batch lot inspection process is more similar to inspection under A astm f2329 inspection of production lots, but Table 1 of F has some additional requirements to consider. Fasteners which are subjected to severe work hardening must be stress-relieved prior to galvanizing.

The major differences between the two specifications, described below, include topics related to sampling protocol, coating thickness, inspection, embrittlement, and documentation.

Referenced Documents purchase separately The documents listed below are referenced within the d2329 standard but are not provided as part of sstm standard.

These astm f2329 can include when steel has been severely work hardened or when the galvanizing bath temperature exceeds the stress relief or tempering temperatures of the fasteners.

Each bolt specification may list additional methods to prevent hydrogen embrittlement as atm as place additional requirements on embrittlement astm f2329 which should astm f2329 researched separately. It is necessary for the astm f2329 to communicate the bath temperature to the customer to ensure the end user understands the effects the galvanizing temperature will have on the steel.

The coating thickness requirements of A Table 1 meet adtm exceed those of F Table 2 except for: According astm f2329 F Paragraph 5. If the customer specifies, the galvanizer will be required to provide the average galvanizing temperature the fasteners will be exposed to. April 10, Authored by Alana Hochstein.

It is informational only and not an official part of the standard; the full text of the standard itself must be referred to for its use and application.

Astm f2329 also provides for minor coating repairs. The ashm thickness requirements of A Table 1 meet or exceed those of F Table 2 except for:. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

Historical Version s – view previous versions of standard. F defines the two different lots and their associated sampling plans as follows: Because A f232 not require water quenching nor chemical post-treatments, communication between the customer and the galvanizer is required to determine whether the galvanizer has a quench tank and the capability to perform chemical post-treatments, or if air-cooling astm f2329 be acceptable.

ASTM F2329 vs. ASTM A153

For each of these types, there are atsm inspection criteria for coating thickness, visual appearance, and adhesion. Coating Thickness Table 2 of F lists average coating thickness requirements for production lots, batch lots, and individual specimens. The acceptance number in all cases is zero defects.

This method is astm f2329 to an inspection of astm f2329 thickness on multi-specimen articles galvanized per ATSM F2239 A summary of the numerical differences between the two awtm related to coating thickness requirements for all materials astm f2329 presented in the table: The type of production lot process will determine which column should be referenced for the sample astm f2329 of each inspection criteria, as summarized in the table below, or per the F Sampling Plan Flow Chart.

Ast, are three columns listing astm f2329 number of test articles for three different inspection tests required under F Adhesion testing is not typically performed when galvanizing to the requirements of A unless there is evidence of an adhesion concern, but F requires adhesion testing stout knife test to be performed astm f2329 the number of articles listed in Table 1, and for every batch lot.

The zinc used for the coating shall conform to the chemical composition required.

Compared to the sampling plan in A, Adtm requires fewer samples per batch lot size, but the galvanizer is required to also conduct adhesion testing and visual inspection for appearance astm f2329 these test articles as defined by Table 1. For long pieces anchor rods astm f2329 articles greater than five feet in lengthcoating thickness measurements must be taken on each end and in the middle of the article.

Quenching According to F Paragraph 5.